metal materials; NdFeB magnet; strip casting
作者:李波,胡季帆,王东玲,郭炳麟,王新林
关键词:metal materials; NdFeB magnet; strip casting; hydrogen decreipitation; nucleation mechanism; rare earths
单位:Department of Functional Materials, Central Iron & Steel Research Institute,Department of Physics, Block neodymium magnet
http://www.chinamagnets.biz/Neodymium/Block-neodymium-magnet.php Shandong University,Department of Functional Materials, Central Iron & Steel Research Institute,Department of Functional Materials, Central Iron & Steel Research Institute,Department of Functional Materials, Central Iron & Steel Research Institute Beijing 100081, China
, Jinan 250100, China
, Beijing 100081, China
, Beijing 100081, China
, Beijing 100081, China
摘要:The coercivity mechanism of Nd Fe B magnets prepared by combination of strip casting with hydrogen decrepitation techniques was investigated. The microstructure of (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 magnet was observed. The average grain size is about 6~12 μm. The magnetizing field dependence of the hardmagnetic properties for the (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 and the temperature dependence of the coercivity for the Nd 14.5 Fe 79.4 B 6.1 were investigated. Results show that the coercivity for magnets prepared by the combination of strip casting with hydrogen decrepitation techniques is controlled by the nucleation mechanism.